Elemental silicon dissolution method to prepare silica sol Business Articles | March 26 Cheap Jameer Nelson Jersey , 2013 The silica sol is a colloidal solution of silica fine particles dispersed in water, also known as silica sol, or silica hydrosol.?
As an important inorganic polymer material, with no curing agent, good durability, improve wettability, strong adsorption, good insulation and other performance, widely used in the chemical, precision casting Cheap Emmanuel Mudiay Jersey , textiles, paper, paints, food, electronics, mineral processing and other fields.
According to metal powder supplier, silicon powder dissolved to prepare silica sol, not only lower costs, with high product purity, also with good stability Cheap Dikembe Mutombo Jersey , is a rise new process for the preparation of sol in recent years. Added the silica fume, deionized water to the flask, and heated to a certain temperature, activated the silicon powder, then added sodium hydroxide, heated and control the reaction temperature, the reaction to a certain period of time, cooling and standing overnight, and then vacuum pumping was filtered off, obtain the sol Cheap Carmelo Anthony Jersey , non-complete reaction silicon powder can be recycled.
Elemental silicon dissolution method using alkali as a catalyst, through the reaction of the silica fume and water, first generated hydrated silicic acid monomer, and then the monomer polymerization was continued into a binary body, trimers, and even polybasic body, finally form of the sol. The sol performance can through its viscosity, Baume degrees (density) and pH values to express. There are many factors affecting the synthesis of silica sol, reaction temperature, reaction time Cheap Allen Iverson Jersey , silica fume and sodium hydroxide dosage will affect the sol preparation.
Temperature has a certain degree influence on the preparation of silica sol, the control of deionized water was used 200mL, silica fume used 25g, sodium hydroxide used 0.16g, the reaction time is 8h, the experiment found, when the temperature lower than 900, the reaction is relatively stable, while the temperature exceeds 900, the reaction is violent Cheap Alex English Jersey , difficult to control. at 65 to 900, sol viscosity and Baume degree gradually increasing, the pH value gradually decreasing, at 900, sol viscosity and Baume degree reaches a maximum, and then gradually decreased, so the preferred temperature of sol preparation is selected 900.
Experimental control of deionized water was used in an amount of 200 ml, silica fume used 25g, sodium hydroxide used 0.16g, the reaction temperature was 900. With the reaction time increasing Wholesale Denver Nuggets Jerseys , the viscosity and Baume degree of the silica sol also gradually increased, and the pH value is gradually reduced. When the reaction temperature is 8h, the viscosity and Baume degree of the silica sol is stabilized, when the reaction time continued to increase, the viscosity and Baume degree of the silica sol, and the pH value did not change a lot, therefore the sol preparation?s better reaction time is 8h.
Experimental control of deionized water was used in an amount of 200ml, and the sodium hydroxide used 0.16g, the reaction temperature was 900°C, the reaction time is 8h Wholesale Nuggets Jerseys , studied the influence of the silicon powder amount on sol preparation, the experimental results indicate that the silicon powder amount have a certain impact on sol viscosity and Baume degrees, and pH, as the silicon powder amount increases, the sol?s viscosity is increasing, but when the silicon powder used in an amount of 25g, the Baume degrees reaches a maximum, thereafter gradually reducing, it is visible that the preferably silicon powder used in an amount of 25g in preparing sol.
Experimental control of deionized water was used in an amount of 200ml, silica fume used 25g Cheap Denver Nuggets Jerseys , the reaction temperature was 900°C, reaction time is 8h, the experimental results show that the amount of catalyst on the silica sol performance has an important influence. If the catalyst amount is too small, it will not achieve the role of the catalyst, also it is not easy to make the reaction generating silica sol; while the amount of the catalyst is too high, the electrostatic repulsion between the colloidal particles reduced, the colloid will merge due to collide, on the contrary, will hinder the formation of the silica sol. So that the sol preparation?s preferred amount of catalyst is 0.16g.
The experimental results show that the preferred process conditions of sol preparation is: added 25g of silicon powder and 0.16g of sodium hydroxide in 200ml of deionized water, to react 8h at a temperature of 900.
Four Myths About Building Self-Confidence Self Help Articles | July 28 Cheap Nuggets Jerseys , 2007 People who have self-confidence believe in themselves and feel that they are capable of achieving what they want in life, or dealing with any situation that they may have to face. They have an aura of self-confidence and self-assurance, which is apparent to others. In contrast, there are many people who are reasonably talented, but who lack self-confidence. These people are victims of the several myths that surround self-confidence.
People who have self-confidence believe in themselves and feel that they are capable of achieving what they want in life, or dealing with any situation that they may have to face. They have an aura of self-confidence and self-assurance, which is apparent to others. People like to spend time with them; they feel comfortable and secure in their presence.
In contrast, there are many people who are reasonably talented, but who lack self-confidence. These people are victims of the several myths that surround self-confidence.
AFK Shakes n Fidget Gilde
Thema drucken
30.12.2019 08:58
Antworten